High Purity White Fused Alumina

20250303

SiO2 ≦0.15% ≦0.15% Na2O ≦0.3% ≦0.2% Fe2O3 ≦0.1% ≦0.1% Bulk?Density >3.55g/cm3 >3.60g/cm3 Physical-Chemical Performance Index Usage Specifics Main Chemical Composition (%) Al2O3 Na2O Fe2O3

CNC Waterjet Abrasive Garnet Sand 80 Mesh for CNC Cutting Machine Use

20240731

SiO2 29% Iron (Fe2O3 +FeO) 31% Alumina Al2O3 17% Magnesium MgO 13% Calcium CaO 8% Manganese MnO < 0.3% Sodium Oxide Na2O 0-1% Titanium Oxide TiO2 1.1% 4. Size 20-40# , 30-60# , 50-80# , 70-100# , 1

Garnet Sand

20150126

Garnet sand a). Chemical composition Wt.% Typical SiO2: 35.0% 37.20% Al2O3: 18.2% 20.59% Fe2O3: 3% 3.73% FeO: 28% 29.49% CaO: 2.50% 2.02% MgO: 5% 6.09% TiO2: 0.5% 0.25% MnO: 1.0% 0.64% K2O:

Mono Crystalline Fused Alumina

20230802

for the grinding and processing of dry mill and easily burned workpiece. Al2O3 ≥99% SiO2 ≥0.07% TiO2 ≥0.45% Fe2O3 ≥0.08% Grit Size:F24,30,36,46,60,80,100,120,180,220 lyn88815 at 163 dot com

Natural Emery Grains

20140603

mineral after diamond according to mohs scale) Al2O3: 62.30 % Fe2O3: 25.60 % SiO2: 8.40 % CaO: 1.20 % MgO: 0.20 % Loss On Ignition: 2.20 % Packaging possible in 50 kg bags or 1000 kg big bags

Brown Fused Alumina

20231117

SiO2 TiO2 Mohs Hardness Bulk Density Specific Gravity BFA-1 92.5-96 0.2-0.5 1.0-2.0 1.5-4.0 9.0 1.53-1.99g/cm3 3.90g/cm3 BFA-2 90-92 1.0-2.0 2.0-4.0 2.0-5.0 BFA-3 70-80 3.0-5.0 5.0-6.0 3.0-6.0 BFA-4

BFA Brown Fused Alumina/Aluminum Oxide/Corundum

20180406

BFA Brown Fused Alumina/Aluminum Oxide/Corundum A GRADE Chemical Analysis(%) Physical Properties Al2O3 92.5-97.0% Specific Gravity 3.90g/cm3 Fe2O3 0.3-1.0% Bulk density 1.53-1.99g/cm3 SiO2 1.0-2.0%

Brown Aluminium Oxide for Grinding Wheel

20210707

Abrasive and Refractory Raw Materials Brown Aluminum Oxide, Brown Fused alumina Item Al2O3 Fe2O3 SiO2 TiO2 Density First Grade 95 % min 0.3 % max 1.5 % max 1.50-3.80 % 3.85 g/cm3 Second Grade 90 %

Brown Aluminium Oxide for Sand Blasting (F14-F1200, P36-P1200)

20180928

SiO2: 1 max; Fe2O3: 0.2 max; TiO2: 3.8 max; CaO: 0.5max; MGO: 0.4 max. Packing: 25kgs/bag or 1000kgs/bag. Chemical Composition (% by weight) Grit No. 16-30 36-60 70-90 100-120 150-180 220 Al2O3 94.5

Brown Aluminium Oxide/Al2O3

20180730

SiO2 TiO2 Magnetic Sandblast Abrasive F-macrogrit 4#-80# ≥95 ≤0.3 ≤1.5 ≤3.0 ≤3.0 90#-150# ≥94.5 ≤3.0 180#-220# ≥94.5 ≤3.5 ≤3.0 Brown aluminaum oxide’s physical pro

Sandblasting Garnet Sand 30/60mesh

20200207

SiO2 34-40% Iron(Fe2O3+FeO) 25-31% Alumina Al2O3 17-21% Magnesium MgO 5-6% Calcium CaO 5.0-10.0% Manganese MnO 0-1.0% Physical Characteristics - Typical...............................................

ZA25 Grit Zirconia Alumina Grit

20210507

SiO2 Max 0.8% Max 0.6% Physical Properties Item ZA25 ZA40 Specific Gravity 4.30g/cm3 4.60g/cm3 Bulk Density 1.90-2.30g/cm3 2.15-2.45g/cm3 Knoop Hardness 1600 1450 Smelting Point 1950 ℃ 1900 ℃ Cry

99% Al2O3 Fused White Corundum Emery Grit 1-3mm 3-5mm

20200406

SiO2(max)0.4Fe2O3(max)0.2Na2O(max)0.4Physical characteristics: colorwhiteMohs Hardness9.0Melting point2250℃Maximum service temperature1900℃Bulk density1.75-1.95g/cm3Real density3.95g/cm3Purpose1

Zirconium Oxide/Zirconium Dioxide CAS 1314-23-4 for Ceramics Powder

20230921

SiO2 %<0.03<0.005<0.02<0.02<0.02TiO2 %<0.01<0.003<0.005<0.005<0.005Water Composition(wt%)<0.5<0.5<1.0<1.0<1.0L.O.I(wt%)<1.0<1.0<3.0<3.0<3.0D50(μm)<5.0<0.5-5<3.0<1.0-5.0<1.0Surface area(m2/g)<73-806-

Brown Fused Alumina Oxide BFA A Fused Corundum Abrasive Industrial

20231013

SiO2TiO2Fe2O3CaOAF4695.720.922.520.060.281050-13500.0091.85F12095.301.122.740.070.271050-13500.0081.62F18094.701.272.930.150.391050-13500.0061.54F36092.421.753.850.620.451050-13500.0221.29A-BF4695.56

CMP Polishing Slurry FInal Polishing Liquid

20231024

SiO2 particles. 2. High removal rate and stable polishing performance. 3. Precision polishing quality with Ra<0.2nm and TTV<0.3um. 4. Cycle use for several times. 5. Applicable to low-temperature p