EC21 Product Catalogs - vickers 10 0

Industry Silicon Carbide(SIC) Ceramic

20250219

10~3.14 3.80 Flexural Strength(4 point bending) (mpa) 400 300 Hardness Vickers (kg/mm2) 2600 1500 Youngs Modulus 410 310 Fracture Toughness (mpa.m1/2) 4.0 2.5 Maximum Working Temperature (℃) 1600

Precision-Engineered Alumina Ceramic Substrates for Automotive Catalysts

20240720

00nm/1mm % 94 Flexural Strength Three Point Bending MPa >350 Fracture Toughness Indentation Method MPa·m1/2 3 Vickers Hardness Load 4.9N GPa 14 Young's Modulus Stretching Method GPa 340 Water Absorp

G5 G10 Si3N4 Ceramic Ball Silicon Carbide Bearing Ball Sic Ceramic Balls

20230912

Silicon Nitride SI3N4 Ceramic balls Diameter range: 0.3 mm – 80 mm Hardness according to Vickers: < 1600(HV10) Temperature resistance: < 1.300°C Density: 3,21 g/cm³Silicon carbide balls(Sic balls

Zirconia Silicate Bead

20141119

10,Φ12,Φ15mm Physical parameters: Composition wt% 60-65% ZrO2; 35% SiO2 Bulk Density Kg/L 2.6～2.7(Φ2mm) Specific Density g/cm3 4.0～4.1 Mohs Hardness Moh's >8.5 Vickers Hardness HV