Sell ETFE +25% Glass Tri packs 2inch

ETFE +25% Glass Tri packs 2inch



ETFE is less flexible than PTFE, but has superior impact strength, abrasion and cut through resistance. Addition of a third component to the chemical structure creates a modified ETFE. For example, ETFE modified by glass fiber reinforcement is tougher and stiffer and has higher tensile strength than PTFE, PFA or FEP. ETFE has a working temperature range of -200°C to 150°C.


Let’s check out property comparison between different fluoropolymers:



Fluoropolymer Produced First in Melting Temperature
°C Tensile Modulus
MPa Elongation at Break
% Dielectric Strength
kV/mm Use Temperature
%
PTFE 1947 317-337 550 300-550 19.7 260
PCTFE 1953 210-215 60-100 100-250 19.7 200
FEP 1960 260-282 345 ~300 19.7 200
PVF 1961 190-200 2000 90-250 12-14 110
PVDF 1961 155-192 1040-2070 50-250 63-67 150
ECTFE 1970 235-245 240 250-300 80 150
ETFE 1973 254-279 827 150-300 14.6 150
THV 1996 145-155 82-207 500-600 48-62 93