Products > compression > Tangshan Polar Bear Building Materials Co.,Ltd. | Similar Products

Your search for "

compression

" found 8 Products from Tangshan Polar Bear Building Materials Co.,Ltd., China

Inquire Now

(1-8 out of 8)

CSA Cement (CSA Binder): Compressive strength (Mpa) 1d ≥60.0 ≥50.0 ≥50.0 3d ≥85.0 ≥75.0 ≥65.0 7d ≥95.0 ≥85.0 ≥75.0 Setting time Initial ≥25min ≥25min ≥25min Final ≤300min ≤300min ≤300min Applications These properties are ...

Light Color CSA Binder (Cement Clinker): Compressive strength (Mpa) 1 day ≥ 50.0 3 days ≥ 75.0 7 days ≥ 85.0 Setting time Initial ≥ 25 min Final ≤ 300 min Chemical Analysis The chemical analysis of LIGHT COLOR CSA BINDER has ...

CSA Cementious Self-Leveling Material: Compressive Strength (Mpa), ≥ 1 day 6.0 6.0 6.0 8 8 7 days 20 20 20 15 15 28 days 30 35 30 25 20 Drying Shrinkage, % ＜0.10 ＜0.05 ＜0.05 ＜0.05 ＜0.05 Bonding Strength ...

CSA Leak-stopping Agent: Compressive Strength (Mpa) 3 days, ≥ 13.0 Flexural Strength (Mpa) 3 days, ≥ 3.0 Impermeability Pressure (Mpa) 7 days ≥ Coating 0.4 Impermeability Pressure (Mpa) 7 days ≥ Check ...

High Strength Non-shrinkage Grouting Material: Compressive Strength (Mpa),≥ 2 hours - - - - - ≥20 4 hours - - - ≥30 ≥20 - 1 day ≥35.0 ≥22.0 ≥20.0 ≥50.0 ≥40.0 ≥55.0 3 ...

CSA Concrete Urgent Repair Material: compressive strength can reach 3.5Mpa within 6h, 35~50Mpa after 28days. 7. Easy to use. The maximum diameter of aggregate in repair material is below 1.5mm; fully apply to all kinds of thin patch. ...

CSA Expansive Agent (Cement Additive): Compressive Strength (Mpa) 7 days 28 days 7 > 40.0 > 54.0 0 37.0 56.5 Longitudinal change of mortar: Application Method 1. Dosage High-efficiency csa expansive agent is used as a part of cement, ...

Rapid Hardening CSA Cement Grade 42.5: Rapid Hardening Cement (Grade 42.5) Introduction General characteristics The product obtained by grinding cement clinker obtained by roasting suitable raw material, consisting essentially of ...