Factory Direct Sale High-strength Wear-resistant Refractory Castable for Cement Kiln: $Factory Direct Sale High-strength Wear-resistant Refractory Castable for Cement Kiln$; SiO2≤3.5Bulk density(g/cm³)110℃ X 24h≥2.7Compressive strength(Mpa)110℃ X 24h≥801100℃ X 3h≥1001400℃ X 3h≥100Flexural strength(MPa)110℃ X 24h≥101100℃ X 3h≥121400℃ X 3h≥12Rate of change of line after ...

Low Price Burned Magnesia Brick - China Refractory Supplier: $Low Price Burned Magnesia Brick - China Refractory Supplier$; SiO2(%)≤1.0≤2.0≤3.5-CaO(%)-≤2.0≤2.0≤3.0Bulk density(g/cm³)≥2.9≥2.95≥2.97≥3.0Apparent porosity(%)≤16≤16≤18≤18Cold Crushing Strength (MPa)≥60≥60≥60≥60refractoiness under load(0.2Mpa ...

Factory Direct Supply Insulating Corundum Mullite Brick Mullite Insulation Brick for Cement Kiln: Introduction of Mullite Insulation BrickSound Proof Mullite Brick, also known as lightweight mullite brick or mullite heat insulation brick, is a high alumina refractory material with mullite (3Al2O3 ...

Aluminum Silicate Board 1260 Degrees Ceramic Fiber Board for Industrial Furnace and Kiln: SiO2≥96≥98≥99≥99--ZrO2--------15-17Al2O3+SiO2+ZrO2--------≥99Fe2O3≤1.0≤0.8≤0.2≤0.2≤0.2Na2O+K2O≤0.4≤0.3≤0.2≤0.2≤0.2CaO+MgO≤0.3≤0.2≤0.2≤0.2≤0.2Working Temp.<1000 ...

High Purity Magnesia Chrome Brick with Factory Price for Furnace Lining: SiO2(%) ≤----------------------Cr2O3(%) ≥810121618Apparent porosity(%) ≤2222201818Bulk density(g/cm³)2.953.003.053.13.1Compressive strength(Mpa) ≥3535353535Degree of softening under load °C ...

Silica Wear-resistant Brick-Silica Mullite Bricks for Cement: SiO2 ≥30 ≥30 ≥30 Al2O3 ≥65 ≥63 ≥60 Bulk Density, g/cm3 ≥2.65 ≥2.6 ≥2.5 Apparent Porosity, % ≤16 ≤17 ≤18 Cold Crushing Strength(MPa) ≥90 ≥90 ≥80 Refractoriness under Load, °C (0.2MPa, ...

High-quality Magnesium Iron Spinel Brick for Cement Rotary Kiln: Sio2 ≤0.8 ≤0.7 cao ≤1.2 ≤1.2 Bulk density(g/cm3) ≥2.97 ≥2.95 Apparent porosity(%) ≤17 ≤17 Normal temperature compressive strength（MPa) ≥70 ≥70 Load softening start temperature (0.2MPa ...

Magnesia-alumina Spinel Bricks Magnesia-alumina Bricks for Cement Kiln: SiO2(%) ≤0.7 ≤0.5 ≤0.35 CaO(%) ≤1.30 ≤1.10 ≤0.95 Bulk density(g/cm³) ≥2.95 ≥2.97 ≥3.0 Apparent porosity(%) ≤16 ≤16 ≤16 Normal temperature compressive strength(MPa) ≥65 ≥65 ≥65 refractoiness under ...