Production Description
DC-A00 Addition silicone is kind of two-component platinum catalyst liquid silicone. The product is Translucent or skin-colored liquid, can be adjusted to any color,and can be very soft and elastomeric after vulcanization.
Application
DC-A00 Addition silicone is mainly used for Breast enhancer, body organ, sex dolls, sex toys, silicone prostheses, silicone mask, ultra-realistic replicas of face, silicone fake skin, silicone animatronic skin, silicone baby mat, silicone baby doll, and so on.
Characteristics
*Good operability, easy to demold
*Moderate hardness
*High tensile and tear strength
*Cure at room temperature
*Good flexibility
*High duplication times
Technical Parameters
1 Datasheet of tin cure silicone rubber
2 Datasheet of platinum cure silicone rubber 
Company Information
Shenzhen Zhihua Chemical Co.,Ltd.(DC SILICONE) are praised as the leading professional manufacturer of Mould Making Silicone Rubber, Addition Silicone Rubber ,Life Casting Silicone Rubber, Electronic Potting Compound, Pad Printing Silicone Rubber, and so on.
Our Factory
Why choose us?
Attractive price to help you save cost High quality with stable performance. Free technical support and sample test to check the quality. More than 10 years experience of silicone rubber producing. Relate products purchasing assistance China visiting reception Factory visiting Reception New market developing New products research and development.
Certificiate
Shelf Life
Twelve(12) months when stored under dry and cool place by original package under 25℃
Package
1kg/can ,5kg/can ,20kg/drum ,25kg/drum ,200kg/durm
Logistics ways
Depending on specific quantity of the order, various logistics ways including the air, the sea and the international express are available.
FAQS
Why isn’t the silicon mold acid & alkali and aging resistant?
It is due to the addition of the silicon oil. Normally we do not advise our customers to add any silicon oil into the silicon rubber. If it is necessary, the ratio must be 5%-10%.
Why is the appearance of the finished mold striate and unsmooth?
It is because the appearance of the product or the model itself is not perfect, and it has not been polished before the further operation. So when you make silicon molds, firstly you should polish the product, spray the mold evenly on the product. In this case, the problem can be avoided.
How to deal with the bubbles during the mixing process?
It depends on your practical situation. Firstly you can deal the mixture with a vacuum machine if you have one; If no such machine, you can reduce the mixing ratio of the hardener from 4% to 1%-2%.Then in the prior period of the reaction of the mixture will be slower, then the air in the mixture will exhaust by itself for a longer curing time to release the bubble.
What should you do for imcomplete curing after the mold is finished?
Two causes lead to this problem: 1 Inexact mixing ratio, not to weigh following the standard ; 2 The mixture of the silicone and catalyst is not mixed evenly. You should avoid this kind of problem ,otherwise there will be a waste of silicone mold.
The solutions of the sticky of the silicone mold?
The main reason for this problem is that you do not handle the products or original molds well, then you should deal with the original mold or products carefully before molding. Such as for the products with a complicated pattern or a unsmoothed surface, you should polish and clean the products after which it will be molded ,then spray the release agent. Normally, the release agent can be Vaseline , detergent. liquid wax Etc. In practical process, you can brush different release agent according to different material. The second reason is that the operator pour the silicone into the mold when the mixture is mixed evenly, then the finish silicone mold will partialy cured.
What should you do for deformation of the silicone mold ?
1 You should choose right silicone rubber with suitable hardness according to the size of the products, In principle, the hardness of the silicone should be consistent to the size of the products.For the small size products with detailed patterns, the soft silicone can be applicable which the shore A should be 15-20 for easy demoulding and not damage of the patterns. Other wise harder silicone should be needed for large size products, such as products with size 50cm will need harder silicone with 40-50 shore A. then no-deformation. If Large products but features detailed patterns then 30 shore A silicone will be workable.(The process should be a layer silicone add a layer fiber glass or cloth..). 2 You should make a outer mold for your silicone mold.The outer of mold can be plaster, glass fiber reinforced plastic(unsaturated resin and fiber glass) to protect the products from deformation.